Project Name
Lindoe Test Specimens
Project Codenumber
UnAssigned
Notes
More information coming soon.
Luke Lindoe Fired Samples
|
Code # L4597 |
Notes
Pictures
Lindoe Cone 10R glaze slip overlay tests
Bodies are H435 and H440
Base glaze: Likely S2 and Celadon
Markings: CR., 25-I, Cry. I.
8-1-40, R.O.M., Mrtl Black
Lindoe Cone 10R glaze tests
#1: Cr I/S2 - Crystal iron red with S2 overlay on H443
#2: Cry Matt - Crystal iron red on H441G
#3: Cr I/S2 - Crystal iron red with S2 overlay on H435
#4: Cr I/GrCel - Crystal iron red with green celadon overlay on H443
#5: BT. 3. Chr - on H440G
#5: 74-61-C - Red Mustard on H440G
Lindoe glazes - 103, 94, 96, 80, 111
94-D, 103-E, 103-D, 96-C2, 80-91 D/2, 111.25, 80-K, 111-96
XML (to paste into Insight)
Born: 2023-01-04, Modified: 2023-03-18 15:57:28
Cone 10R Celadon - Luke Lindoe
|
Code # 77E05B |
| Materials | Amt |
|---|---|
| Custer Feldspar | 27.000 |
| Calcium Carbonate | 20.000 |
| EPK | 20.000 |
| Silica | 33.000 |
| Additions | |
|---|---|
| Iron Oxide Red | 1.000 |
Total:101.00
Auto Unity Formula
|
Si:Al: 8.5:1 6.7 (Molar:6.4) 11.9 Cost 0.23 per kg |
Notes
This recipe was used, and possibly developed, by Luke Lindoe.
He used as much from 1-5% iron for light to dark green colors.
This did craze on some bodies, one simple change to improve it would be to use 325 mesh silica (increase of 200 mesh).
Pictures
Lindoe Cone 10R glaze slip overlay tests
Bodies are H435 and H440
Base glaze: Likely S2 and Celadon
Markings: CR., 25-I, Cry. I.
8-1-40, R.O.M., Mrtl Black
Lindoe Cone 10R glaze tests
#1: Cr I/S2 - Crystal iron red with S2 overlay on H443
#2: Cry Matt - Crystal iron red on H441G
#3: Cr I/S2 - Crystal iron red with S2 overlay on H435
#4: Cr I/GrCel - Crystal iron red with green celadon overlay on H443
#5: BT. 3. Chr - on H440G
#5: 74-61-C - Red Mustard on H440G
Lindoe celadon (light and dark versions)
The dark had about 5% iron, the light about 3%.
Typecodes
RCP-Undefined
Alternate Code Number:G 140
XML (to paste into Insight)
<?xml version="1.0"?> <recipes version="1.0" encoding="UTF-8"> <recipe name="Cone 10R Celadon - Luke Lindoe" id="71931" key="rdfnGaZB" date="2023-03-18" typecodes="RCP" codenum="77E05B" picturebasename=""> <recipelines> <recipeline material="Custer Feldspar" amount="27.000" tolerance=""/> <recipeline material="Calcium Carbonate" amount="20.000" tolerance=""/> <recipeline material="EPK" amount="20.000" tolerance=""/> <recipeline material="Silica" amount="33.000" tolerance=""/> <recipeline material="Iron Oxide Red" amount="1.000" added="true"/> </recipelines> </recipe> </recipes>
Born: 1990-02-13, Modified: 2023-03-18 13:02:16
Cone 10R S2 - Luke Lindoe
|
Code # G3966 |
| Materials | Amt |
|---|---|
| Custer Feldspar | 32.000 |
| Calcium Carbonate | 15.000 |
| PR #3B (B Clay) | 15.000 |
| 45D (IXL 45D) | 15.000 |
| Silica | 20.000 |
| Additions | |
|---|---|
| Bentonite | 3.000 |
Total:100.00
Auto Unity Formula
|
Si:Al: 9.6:1 6.8 (Molar:6.4) 9.3 |
Notes
Custer 30.5
856 Metallic Black Glaze 19.0
45D 8.0
Silica 12.5
Calcium carbonate 15.0
Frit 3134 15.0
Frit 3498 3.75 ( 80% lead)
Bentonite 2.25
CMC Gum .1
RED:
Copper carb .6
Tin oxide 3
Cone 10, ball mill for 2 hours. Begin reduction apprx. when cone 10 goes down to 45degree angle, reduce for 40 minutes.
Received from Sebet Lindoe
Pictures
Lindoe Cone 10R glaze tests
#1: Cr I/S2 - Crystal iron red with S2 overlay on H443
#2: Cry Matt - Crystal iron red on H441G
#3: Cr I/S2 - Crystal iron red with S2 overlay on H435
#4: Cr I/GrCel - Crystal iron red with green celadon overlay on H443
#5: BT. 3. Chr - on H440G
#5: 74-61-C - Red Mustard on H440G
Lindoe Cone 10R glaze slip overlay tests
Bodies are H435 and H440
Base glaze: Likely S2 and Celadon
Markings: CR., 25-I, Cry. I.
8-1-40, R.O.M., Mrtl Black
Lindoe S2 copper red with 4.5, 6% tin oxide
Fired at cone 10R on H555.
There seems to be little difference in the surface.
Lindoe S2 Copper Red at cone 10R
The code number might be 102-B
Lindoe S2 cone 10R glaze
Lindoe 85-6 Blue S2 glaze cone 10R
S2/99-9 and 99-10 Lindoe cone 10R glazes
Typecodes
RCP-Undefined
XML (to paste into Insight)
<?xml version="1.0"?> <recipes version="1.0" encoding="UTF-8"> <recipe name="Cone 10R S2 - Luke Lindoe" id="63672" key="xT383xQK" date="2023-03-18" typecodes="RCP" codenum="G3966" picturebasename=""> <recipelines> <recipeline material="Custer Feldspar" amount="32.000" tolerance=""/> <recipeline material="Calcium Carbonate" amount="15.000" tolerance=""/> <recipeline material="PR #3B" lookup="B Clay" amount="15.000" tolerance=""/> <recipeline material="45D" lookup="IXL 45D" amount="15.000" tolerance=""/> <recipeline material="Silica" amount="20.000" tolerance=""/> <recipeline material="Bentonite" amount="3.000" added="true"/> </recipelines> </recipe> </recipes>
Born: 2003-06-05, Modified: 2023-03-18 14:12:57
Cone 10R Crystal Iron Brown - Luke Lindoe
|
Code # G 304 |
| Materials | Amt |
|---|---|
| Custer Feldspar | 50.000 |
| Calcium Carbonate | 15.000 |
| 45D (IXL 45D) | 20.000 |
| PR3B (B Clay) | 10.000 |
| Additions | |
|---|---|
| Bentonite | 2.500 |
| Rutile | 5.000 |
| Iron Oxide Red | 10.000 |
Total:112.50
Auto Unity Formula
|
Si:Al: 6.7:1 8.6 (Molar:7.8) 10.0 |
Notes
Pictures
Lindoe Cone 10R glaze tests
#1: Cr I/S2 - Crystal iron red with S2 overlay on H443
#2: Cry Matt - Crystal iron red on H441G
#3: Cr I/S2 - Crystal iron red with S2 overlay on H435
#4: Cr I/GrCel - Crystal iron red with green celadon overlay on H443
#5: BT. 3. Chr - on H440G
#5: 74-61-C - Red Mustard on H440G
Typecodes
RCP-Undefined
XML (to paste into Insight)
<?xml version="1.0"?> <recipes version="1.0" encoding="UTF-8"> <recipe name="Cone 10R Crystal Iron Brown - Luke Lindoe" id="63671" key="JM2L3FQW" date="2023-01-06" typecodes="RCP" codenum="G 304" picturebasename=""> <recipelines> <recipeline material="Custer Feldspar" amount="50.000" tolerance=""/> <recipeline material="Calcium Carbonate" amount="15.000" tolerance=""/> <recipeline material="45D" lookup="IXL 45D" amount="20.000" tolerance=""/> <recipeline material="PR3B" lookup="B Clay" amount="10.000" tolerance=""/> <recipeline material="Bentonite" amount="2.500" added="true"/> <recipeline material="Rutile" amount="5.000" added="true"/> <recipeline material="Iron Oxide Red" amount="10.000" added="true"/> </recipelines> </recipe> </recipes>
Born: 1980-01-01, Modified: 2023-01-06 11:05:28
Cone 10R Matte Crystal Iron - Luke Lindoe
|
Code # 84-G-05-S |
| Materials | Amt |
|---|---|
| Custer Feldspar | 38.816 |
| Soda Feldspar | 18.413 |
| Kaolin | 25.380 |
| Dolomite | 12.939 |
| Talc | 1.742 |
| Tricalcium Phosphate | 1.742 |
| Additions | |
|---|---|
| Tin Oxide | 4.479 |
| Iron Oxide Red | 1.891 |
Total:105.40
Auto Unity Formula
|
Si:Al: 4.4:1 7.2 (Molar:6.9) 9.7 |
Notes
Pictures
Lindoe Cone 10R glaze tests
#1: Cr I/S2 - Crystal iron red with S2 overlay on H443
#2: Cry Matt - Crystal iron red on H441G
#3: Cr I/S2 - Crystal iron red with S2 overlay on H435
#4: Cr I/GrCel - Crystal iron red with green celadon overlay on H443
#5: BT. 3. Chr - on H440G
#5: 74-61-C - Red Mustard on H440G
Typecodes
RCP-Undefined
XML (to paste into Insight)
<?xml version="1.0"?> <recipes version="1.0" encoding="UTF-8"> <recipe name="Cone 10R Matte Crystal Iron - Luke Lindoe" id="63532" key="coeGv7H8" date="2023-01-06" typecodes="RCP" codenum="84-G-05-S" picturebasename=""> <recipelines> <recipeline material="Custer Feldspar" amount="38.816" tolerance=""/> <recipeline material="Soda Feldspar" amount="18.413" tolerance=""/> <recipeline material="Kaolin" amount="25.380" tolerance=""/> <recipeline material="Dolomite" amount="12.939" tolerance=""/> <recipeline material="Talc" amount="1.742" tolerance=""/> <recipeline material="Tricalcium Phosphate" amount="1.742" tolerance=""/> <recipeline material="Tin Oxide" amount="4.479" added="true"/> <recipeline material="Iron Oxide Red" amount="1.891" added="true"/> </recipelines> </recipe> </recipes>